| Quantity: | |
|---|---|
HLD T800
Honglida
| Item | Test method | Performance |
| color | Visual estimation | green |
| thickness | ASTM D1000 | ≥1.8mm |
| application temperature range | ----- | -45~70°C |
| Specific Insulation Resistance | EN 12068 | ≥108Ω.m2 |
| Dielectric strength | DIN 53481 | ≥10kv/mm |
| peel strength @ (23 ℃) to PE to Steel to FBE | ISO 21809-3 | 4N/cm 5N/cm 6N/cm |
| Lap Shear @ 23℃ | ISO 21809-3 | 0.04N/mm2 |
| Water Absorption | ASTM D 570 | 0.03% |
| Impact Resistance | EN 12068 | > 15J |
| Cathodic Disbandment | EN 12068 | ≤20 mm-rad |
| Drip Resistance @85 ℃ for 72 hours | ----- | No dripping |
| Chemical Resistance 10% HCL,10%Na OH, 3%NaCL for 90 days | ----- | Pass |
| Hot water immersion @60℃ for 120 days | ---- | Pass |
| Item | Test method | Performance |
| color | Visual estimation | green |
| thickness | ASTM D1000 | ≥1.8mm |
| application temperature range | ----- | -45~70°C |
| Specific Insulation Resistance | EN 12068 | ≥108Ω.m2 |
| Dielectric strength | DIN 53481 | ≥10kv/mm |
| peel strength @ (23 ℃) to PE to Steel to FBE | ISO 21809-3 | 4N/cm 5N/cm 6N/cm |
| Lap Shear @ 23℃ | ISO 21809-3 | 0.04N/mm2 |
| Water Absorption | ASTM D 570 | 0.03% |
| Impact Resistance | EN 12068 | > 15J |
| Cathodic Disbandment | EN 12068 | ≤20 mm-rad |
| Drip Resistance @85 ℃ for 72 hours | ----- | No dripping |
| Chemical Resistance 10% HCL,10%Na OH, 3%NaCL for 90 days | ----- | Pass |
| Hot water immersion @60℃ for 120 days | ---- | Pass |